Nickel Alloy 200 Round Bars

UNS N02200 Round Bar, DIN 2.4066 Rods

We are Manufacture, Suplier & Export of Nickel Alloy 200 Round Bars in form of Round, Square, Hex (A/F), Bush, Rectangle, Flat, and Wire Mesh. Nickel 200 bars are commercially pure wrought nickel with good mechanical properties and resistance to a variety of corrosive environments. Nickel 200 Round Bars are created from high-quality standard raw materials and engineered to meet national and international standards. Alloy 200 Round Bars are corrosion resistant in reducing, neutral, and oxidizing atmospheres, as long as the oxidizing environment allows for the production of a passive oxide film. Our Alloy 200 Round Bars (UNS N02200) are used for quite a lot of applications in different industries like Marine, Pulp and Paper, Aerospace, Petrochemical, Chemical Processing, Oil and Gas, Waste processing, Food Processing, and Power generation Industries.

Nickel 200 can be hot formed to almost any shape Round Bar. The temperature range 1200°F to 2250°F is recommended and should be carefully abided as the proper temperature is the most important factor in achieving hot malleability. Nickel 200 Square Bars is a commercial unalloyed nickel with excellent corrosion resistance and low electrical resistivity.

Specification Of Nickel Alloy 200 Round Bars

Dimensions DIN, EN, ASTM, JIS, ASME, BS, AISI
Standard ASTM B160, ASME SB160
Hex Bar size 2-100mm A/F
Round bar size Diameter: 3-~800mm
Flat bar size Thickness: 2 -100mm
Width: 10 to 500mm
Angle bar size 3mm*20mm*20mm~12mm*100mm*100mm
Square bar size 4 to 100mm
Channel Bar 80 x 40mm to 150 x 75mm section; 5.0 to 6.0mm thickness
Rectangular Bars Section 3.0 to 12.0mm thickness
Threaded Bar Billet Size 1/2 to 495mm Diameter
Rectangles Size 33 x 30mm to 295 x 1066mm
Hollow Bar 32mm OD x 16mm ID to 250mm OD x 200mm ID)
Tolerance H8, H9, H10, H11, H12, H13K9, K10, K11, K12 or as per clients’ requirements
Finish Cold (bright) drawn, centreless ground, hot rolled, smooth turned, peeled, slit rolled edge, hot rolled annealed, Rough Turned, Bright, Polish, Grinding, Centreless Ground & Black
Surface Hot Rolled Pickled, Bright, Sand Blasting Finished, Cold Drawn, Hairline,Polished
Condition Hardened & tempered, annealed
Technique Cold Drawn, Hot Rolled, Forged Round Bar,Cold Rolled, Rod
Processing Bar cutting to 650mm
Form Rod, Round, Channel Bar, T-Bar, Flat Bar, Precision Ground Bar, Blocks, Square, Rings, Round Rod, Triangle, Hollow, Rectangle, Threaded, Hex (A/F), Profiles, Half Round Bar, Ingot, Billet, I/H Bar, Forging etc.

Equivalent Grades

STANDARD WERKSTOFF NR. UNS JIS BS GOST AFNOR EN
Nickel 200 2.4066 N02200 NW 2200 NA 11 НП-2 N-100M Ni 99.2

Chemical Composition

Grade C Mn Si Cu S Fe Mo Ni Cr
Nickel 200 0.15 max 0.35 max 0.35 max 0.25 max 0.01 min 0.40 max – 99 min –

Mechanical Properties

Density Melting Point Tensile Strength Yield Strength (0.2%Offset) Elongation
8.9 g/cm3 1446 °C (2635 °F)  Psi – 67,000 , MPa – 462 Psi – 21,500 , MPa – 148 45 %