Nickel Alloy 200 Sheets Plates

UNS N02200 Plate, DIN 2.4066 Sheets

We are Manufacturer, Supplier & Exporter of Alloy 200 Sheet Plate / Structural, which has outstanding confrontation to corroding alkalis at a number of concentrations and temperatures. Alloy 200 Structural is an amendment of Nickel 200 to regulate carbon content that retains it from embrittled by intergranular hastens at temp of 600 Deg F to 1400 Deg F in a lot of procedures. After obtaining raw materials from trustworthy vendors, we use technologies such as solid solution strengthening to manufacture Nickel Alloy 200 Sheets. Our Nickel Alloy 200 Shim Sheets maintain their strength and vigour even at high temperatures. On the other hand, our Nickel Alloy 200 Perforated Sheets and High Nickel Alloy 200 Hot Rolled Sheets are resistant to a variety of harmful corrosions.

These Nickel 200 Plates (UNS N02200) can be hot-formed into any shape and cold-formed using any process. Alloy 200 Sheets are commercially pure nickel with good corrosion resistance and a low electrical resistivity. Alloy 200 Plates' low electrical resistivity has made them suitable for usage as conducting leads and terminals in electrical and electronic components. Nickel 200 Sheets are used at temperatures above 315 degrees Celsius because of their increased resistance to "creep."

Specification Of Nickel Alloy 200 Sheets & Plates

Specifications ASTM B127 / ASME SB127, BS EN 10088-2, en 10028-7, IS 6911
Dimension Standard MSRR, AMS, BS, JIS, AISI, ASTM, GB, DIN, EN, etc
Size Range Cold rolled Plate 0.5-6.4 mm
Hot rolled Plate 3.0–10.0 mm
Width 1000mm, 1219mm, 1500mm, 1800mm, 2000mm, 2500mm, 3000mm, 3500mm, etc
Length 2000mm, 2440mm, 3000mm, 5800mm, 6000mm, etc
Thickness 0.3 mm to 120 mm
International Standard ASTM A480
ASTM A959
ASME IID
EN ISO 9445
EN ISO 18286
EN 10051
EN 10088-1
ISO 15510
Tolerances (width / thickness) EN 10258/ DIN 59381)
EN 10151
EN 10088
Finish 2B, 2D, BA NO (8), Cold rolled Plate (CR), Hot rolled plate (HR), SATIN (Met with Plastic Coated), No.1 finish hot rolled, 1D, 2B, No.4, BA, 8K, satin, hairline, brush, mirror etc.
Hardness Half Hard, Soft, Hard, Quarter Hard, Spring Hard
Value Added Service Cladding, Heat Treatment, Annealed, Pickling, Polish, Rolling, Cutting, Bending, Forging, Minor Fabrication Etc.
Dealers & Distributor of SAIL, ESSAR, JINDAL, TATA, BHUSHAN, INDIAN, POSCO, JISCO, TISCO, LISCO, BAOSTEEL IMPORTED material
Profiling Plasma Plate Cutting
Laser Plate Cutting
Oxy-propane Flame Cutting

Equivalent Grades

STANDARD WERKSTOFF NR. UNS JIS BS GOST AFNOR EN
Nickel 200 2.4066 N02200 NW 2200 NA 11 НП-2 N-100M Ni 99.2

Chemical Composition

Grade C Mn Si S Cu Fe Ni
Nickel 200 0.15 max 0.35 max 0.35 max 0.01 max 0.25 max 0.40 max 99.0 min

Mechanical Properties

Element Density Melting Point Tensile Strength Yield Strength (0.2%Offset) Elongation
Nickel 200 8.9 g/cm3 1446 °C (2635 °F) Psi – 67000 , MPa – 462 Psi – 21500 , MPa – 148 45 %