Nickel Alloy 200 Pipe Tubes

UNS N02200 Pipes, DIN 2.4066 Pipes

Manufacturer, Supplier & Exporter of quality Nickel 200 Pipes & Tubes, which is commercially pure (99.6 %) wrought nickel. Nickel Alloy 200 Tubes normally limited to service at temperatures below 600 Degree F. Meanwhile at superior temperatures, Nickel 200 Pipes can writhe from graphitization that can outcome in sternly compromised properties. Nickel alloy 200 pipes tubes of a high quality of tubes that can be used effectively in industries. Nickel 200 Welded Pipes is a commercially pure nickel that exhibits good corrosion resistance and has rather low electrical resistivity. Meanwhile, these Nickel 200 EFW Pipes are also being offered in different sizes and shapes to our customers. The lower content of carbon of Nickel UNS N02200 Pipes Tubes makes it very resistant and so is less subject to embrittlement.

Alloy 200 Seamless Tubes are approved for construction of pressure vessels and components, where melting point is 2615 Degree F – 2635 Degree F. We offer these Nickel 200 pipes & tubes are available in different size, grades, specification & Thickness as per the clients requirements. These pipes & tubes widely used in various applications industry like oil & gas, drilling & well building and chemical industries etc.

Specification Of Nickel Alloy 200 Pipes & Tubes

200 Pipes Specifications ASTM B161, B517, B161, B516 / ASME SB161, SB517, SB161, SB516
Dimensional specification ANSI/ASME B36.19M, ANSI/ASME B36.10M
ASTM B161 B161 200 Seamless Pipe & Tube Size 1 / 2" NB - 16" NB
ASTM B161 B161 200 Welded Pipe & Tube Size 1 / 2" NB - 24" NB
ASTM B517 B516 200 EFW Pipe & Tube Size 6" NB - 24" NB
Outside Diameter 6.00 mm OD up to 914.4 mm OD, Sizes up to 24” NB available Ex-stock, OD Size Steel Tubes available Ex-stock
Nickel Alloy 200 Pipes & Tubes Manufacturing Shapes Hydraulic, Round, Rectangle, Square, Hex, Honed
Nickel Alloy 200 Pipes & Tubes Manufacturing Techniques Seamless / Welded / ERW / Fabricated / CDW / 100% X Ray Welded
Nickel Alloy 200 Pipes & Tubes Schedule Thickness Range SCH 5, SCH10, SCH 40, SCH 80, SCH 80S, SCH 160, SCH XXS, SCH XS
Nickel Alloy 200 Pipes & Tubes End Types Plain End, Beveled End, Treaded One End, TBE (Treaded Both Ends)
Delivery Condition of Nickel Alloy 200 Pipes & Tubes Annealed and Pickled, Polished, Bright Annealed, Cold Drawn
Surface Finish No.1, No.4, No.8 Mirror Finish, 2B
Value Added Services Cutting, Beveling, Polishing, Threading, Destructive, Non Destructive, Ultrasonic Testing
Inspection and Test Reports EN 10204 3.1, Mill Test Certificates, Chemical Reports, PMI Test Reports, Mechanical Reports, Third Party Inspection, NABL Approved Lab, Visual Inspection, Destructive Test and Non Destructive Test Reports
Marking Specification
Grade
Nominal Pipe Sizes
Pipe Schedule or Wall Thickness
Manufacturing Method (Seamless / Welded)
Heat Number
Manufacturer’s Name or Custom Logo - on request
Marked Pipe Sample: ANSI B36.19 ASTM A 312 TP 200 12" NB SCH 40S SEAMLESS HEAT NO. XXXX
Outside Finish 2B, No.4, No.1, No.8 Mirror Finish for Nickel Alloy Pipes, Finish as per customer Requirements
Delivery Condition Annealed and Pickled, Polished, Bright Annealed, Cold Drawn
Packing of Nickel Alloy 200 Pipes & Tubes Packed in Wooden Boxes, Plastic Bags, Steel Strips Bundled, or as per Customers Requests
Specials Sizes and Specifications other than above can be on request

Equivalent Grades

STANDARD UNS WERKSTOFF NR. AFNOR EN JIS BS GOST
Nickel 200 N02200 2.4066 N-100M Ni 99.2 NW 2200 NA 11 НП-2

Chemical Composition

Nickel 200 Ni C Mo Mn Si Fe P S Cu Cr
99.0 min 0.15 max – 0.35 max 0.1 max 0.4 max – 0.01 max 0.25 max –

Mechanical Properties

Density Melting Point Yield Strength (0.2%Offset) Tensile Strength Elongation
8.9 g/cm3 1446 °C (2635 °F) Psi – 21500 , MPa – 148 Psi – 67000 , MPa – 462 45 %