Inconel 800 Sheets Plates

UNS N08800 / N08810 / N08811 Plate, DIN 1.4876 / 1.4958 Sheets

Mangalam Metal is manufacturer and trader of Incoloy Alloy 800 / 800H / 800HT Sheets & Plates, which is widely used in the chemical field and petrifaction field, such as the element of chloride organic and catalyzes system. Altogether, it works together to provide excellent resistance in Incoloy 800 Sheets to non-oxidizing acids and cracking due to corrosion. This offered range of Incoloy 800H Plates is manufactured by making use of premium quality required basic material and components, procured from the accredited experts of the industry, astheir sincere efforts have enabled us in attaining maximum satisfaction of the entire client-base we hold. Incoloy 800HT Coils has exceptional resistance to a wide variety of chemical process environments, including strong oxidizers such as ferric and cupric chlorides, hot contaminated media (organic and inorganic), chlorine, formic and acetic acids, acetic anhydride, and seawater and brine solutions. For optimum corrosion resistance in Incoloy 800 Perforated Plates, forged parts should be subsequently annealed.

Incoloy 800H Sheets is used for evaporators, heat exchangers, filters and mixers used in sulfuric acid environments, sulfuric acid reactors, and organic chloride process equipment, equipment for processes utilizing halide or acid catalysts. All tests for Incoloy 800HT Plates were performed in reagent grade acids under laboratory conditions; field tests are encouraged prior to industrial use.

Specification Of Incoloy 800 / 800H / 800HT Sheets & Plates

Grade Incoloy 800, 800H, 800HT | UNS N08800, N08810, N08811
Standard ASTM B409 / ASME SB409
Size 1000 mm x 2000 mm, 1220 mm x 2440 mm, 1500 mm x 3000 mm, 2000 mm x 2000 mm, 2000 mm x 4000 mm
Thickness 0.1mm To 100 mm
Finish Hot rolled plate (HR), Cold rolled sheet (CR), 2B, 2D, BA NO(8), SATIN (Met with Plastic Coated)
Form Sheets, Plates, Coils, Slatting Coils, Perforated Coils, Foils, Rolls, Plain Sheet, Shim Sheet, Strip, Flats, Blank (Circle), Ring (Flange)
Hardness Soft, Hard, Half Hard, Quarter Hard, Spring Hard etc.

Equivalent Grades

STANDARD WERKSTOFF NR. UNS JIS BS GOST AFNOR EN OR
Incoloy 800 1.4876 N08800 NCF 800 NA 15 ЭИ670 Z8NC32-21 X10NiCrAlTi32-20 XH32T
Incoloy 800H 1.4958 / 1.4876 N08810 NCF 800H NA 15(H) ЭИ670 Z8NC33-21 X5NiCrAlTi31-20 XH32T
Incoloy 800HT 1.4859 / 1.4876 N08811 NCF 800HT NA 15(HT) ЭИ670 - X8NiCrAlTi32-21 XH32T

Chemical Composition

Grade C Mn Si S Cu Fe Ni Cr Al Ti
800 0.10 max 1.50 max 1.00 max 0.015 max 0.75 max 39.50 min 30.00 – 35.00 19.00 – 23.00 0.15 – 0.60 0.15 – 0.60
800H 0.05 – 0.10 1.50 max 1.00 max 0.015 max 0.75 max 39.50 min 30.00 – 35.00 19.00 – 23.00 0.15 – 0.60 0.15 – 0.60
800HT 0.06 – 0.10 1.50 max 1.00 max 0.015 max 0.75 max 39.50 min 30.00 – 35.00 19.00 – 23.00 0.15 – 0.60ᴬ 0.15 – 0.60ᴬ

Mechanical Properties

Element Density Melting Point Tensile Strength Yield Strength (0.2%Offset) Elongation
800 / 800H / 800HT 7.94 g/cm3 1385 °C (2525 °F) Psi – 75,000 , MPa – 520 Psi – 30,000 , MPa – 205 30 %