Hastelloy B3 Sheets Plates

UNS N010675 Plate, DIN 2.4600 Sheets

Mangalam Metal is manufacturer and distributor of Hastelloy Alloy B3 Sheets and Plates, which can be used at temperatures above 540 Degree C (1000 Degree F). Hastelloy B3 Plates has a higher Chromium level, demonstrating improved corrosion resistance in oxidizing aqueous media when high levels of chloride ions are present. Hastelloy B3 Coils which have been hot formed or severely cold formed should be heat treated at 2050 degree F and rapid quenched prior to final fabrication or installation. Alloy B3 Plates has a high work hardening rate, and efficient machining requires rigid and over powered machines, sharp tools, preferably carbide-tipped, and heavy, constant feeds. Alloy B3 Coils has outstanding resistance to a wide variety of chemical process environments including ferric and cupric chlorides, hot contaminated mineral acids, solvents, chlorine and chlorine contaminated (both organic and inorganic), dry chlorine, formic and acetic acids, acetic anhydride, sea water and brine solutions and hypochlorite and chlorine dioxide solutions.

Hastelloy B3 Perforated Sheets is used in Acid cleaning system, Plate heat exchanger, Selectivity filter system, Sulfur dioxide cooling tower, Sulfonating system, Tubing heat exchanger, Resurfacing welding valve, etc. The lowest temperature at which pitting has been observed UNS N010675 Plate is 120 Degree C. DIN 2.4600 Sheets resists the formation of grain-boundary precipitates in the weld heat-affected zone. Hastelloy B3 Slatting Sheets has key alloying elements are chromium, molybdenum and tungsten.

Specification Of Hastelloy B3 Sheets & Plates

Specifications ASTM B333 / ASME SB333, BS EN 10088-2, en 10028-7, IS 6911
Dimension Standard MSRR, AMS, BS, JIS, AISI, ASTM, GB, DIN, EN, etc
Size Range Cold rolled Plate 0.5-6.4 mm
Hot rolled Plate 3.0–10.0 mm
Width 1000mm, 1219mm, 1500mm, 1800mm, 2000mm, 2500mm, 3000mm, 3500mm, etc
Length 2000mm, 2440mm, 3000mm, 5800mm, 6000mm, etc
Thickness 0.3 mm to 120 mm
International Standard ASTM A480
ASTM A959
ASME IID
EN ISO 9445
EN ISO 18286
EN 10051
EN 10088-1
ISO 15510
Tolerances (width / thickness) EN 10258/ DIN 59381)
EN 10151
EN 10088
Finish 2B, 2D, BA NO (8), Cold rolled Plate (CR), Hot rolled plate (HR), SATIN (Met with Plastic Coated), No.1 finish hot rolled, 1D, 2B, No.4, BA, 8K, satin, hairline, brush, mirror etc.
Hardness Half Hard, Soft, Hard, Quarter Hard, Spring Hard
Value Added Service Cladding, Heat Treatment, Annealed, Pickling, Polish, Rolling, Cutting, Bending, Forging, Minor Fabrication Etc.
Dealers & Distributor of SAIL, ESSAR, JINDAL, TATA, BHUSHAN, INDIAN, POSCO, JISCO, TISCO, LISCO, BAOSTEEL IMPORTED material
Profiling Plasma Plate Cutting
Laser Plate Cutting
Oxy-propane Flame Cutting

Equivalent Grades

STANDARD WERKSTOFF NR. UNS
Hastelloy B3 2.4600 N010675

Chemical Composition

Grade Ni Mo Cr Fe W Mn C Al Ti Si
Hastelloy B3 65.0 min 28.5 1.5 1.5 3.0 max 3.0 max 0.01 max 0.50 max 0.2 max 10 max

Mechanical Properties

Density Melting Point Tensile Strength Yield Strength (0.2%Offset) Elongation
9.2 g/cm3 1370 °C (2550 °F) Psi – 1,15,000 , MPa –760 Psi – 52,000 , MPa – 350 40%